Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP AP3N EXXONMOBIL SINGAPORE
ExxonMobil™
Electrical appliances、Home appliance components、Consumer goods sector、Consumer product applicat
High rigidity、High gloss、Middle flow、Fast forming cycle
UL
TDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EXXONMOBIL SINGAPORE/AP3N |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.6 kJ/m² |
| -30°C | ISO 179/1eA | 3.6 kJ/m² | |
| -20°C | ISO 179/1eA | 4.0 kJ/m² | |
| Dart impact | -29°C,3.18mm | ASTM D5420 | 18.0 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.3 kJ/m² |
| -40°C | ISO 180/1A | 3.8 kJ/m² | |
| Charpy Notched Impact Strength | 0°C | ISO 179/1eA | 4.5 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256A | 96 J/m |
| -18°C | ISO 180/1A | 4.5 kJ/m² |
| hardness | Test Condition | Test Method | EXXONMOBIL SINGAPORE/AP3N |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 98 |
| Mechanical properties | Test Condition | Test Method | EXXONMOBIL SINGAPORE/AP3N |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1690 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 28.2 Mpa |
| Flexural modulus | 1%正割5 | ASTM D790B | 1710 Mpa |
| tensile strength | 屈服3 | ASTM D638 | 28.8 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 5.0 % |
| 屈服3 | ASTM D638 | 5.0 % | |
| Flexural modulus | --6 | ISO 178 | 1510 Mpa |
| 1%正割4 | ASTM D790A | 1480 Mpa |
| physical property | Test Condition | Test Method | EXXONMOBIL SINGAPORE/AP3N |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | EXXONMOBIL SINGAPORE/AP3N |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 114 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 54.0 °C | |
| 0.45MPa,退火，HDT | ASTM D648 | 123 °C | |
| 0.45MPa,未退火，HDT | ISO 75-2/Bf | 100 °C |