HDPE TIPELIN® BS 501-17 MOL Petrochemicals Co. Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 501-17 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 15 kJ/m² |
| hardness | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 501-17 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 64 |
| Mechanical properties | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 501-17 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 35.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 1100 % |
| tensile strength | 屈服 | ISO 527-2 | 27.0 MPa |
| Flexural modulus | ISO 178 | 1400 MPa |
| physical property | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 501-17 |
|---|---|---|---|
| Environmental stress cracking resistance | 10%IgepalCO-630,F50 | ASTM D1693B | 160 hr |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 0.94 g/10min |
| density | ISO 1183 | 0.950 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.20 g/10min |
| 190°C/21.6kg | ISO 1133 | 23 g/10min |
| Thermal performance | Test Condition | Test Method | MOL Petrochemicals Co. Ltd./TIPELIN® BS 501-17 |
|---|---|---|---|
| Oxygen induction time | 200°C | EN728 | 7.0 min |
| vicat | ISO 306/A120 | 127 °C |