Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM GC25A BK CELANESE USA
CELCON®
Electrical field,Electronic field
enhance,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| linear expansion coefficient | Test Condition | Test Method | CELANESE USA/GC25A BK |
|---|---|---|---|
| horizontal | IISO 11359-2 | E-4/℃ |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/GC25A BK |
|---|---|---|---|
| tensile strength | 5mm/min | ISO 527-2/1A | 106 Mpa |
| Charpy Notched Impact Strength | -30℃ | ISO 179/1eU | 35 kJ/m² |
| Tensile strain | 5mm/min | ISO 527-2/1A | 2 % |
| Flexural modulus | 23℃ | ISO 178 | 8700 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 25 kJ/m² |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 6.0 kJ/m² |
| Tensile modulus | 1mm/min | ISO 527-2/1A | 8600 Mpa |
| bending strength | 23℃ | ISO 178 | 160 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 6.4 kJ/m² |
| physical property | Test Condition | Test Method | CELANESE USA/GC25A BK |
|---|---|---|---|
| Water absorption rate | 23℃,50%相对湿度 | ISO 62 | 0.2 % |
| Shrinkage rate | 横向 | ISO 294-4 | 0.4 % |
| Water absorption rate | 23℃,饱和 | ISO 62 | 0.8 % |
| Shrinkage rate | 纵向 | ISO 294-4 | 1.2 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/GC25A BK |
|---|---|---|---|
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 160 °C |
| melting temperature | ISO 11357-1 | 165 °C | |
| Linear coefficient of thermal expansion | 纵向 | ISO 11359-2 | 1.2 E-4/℃ |
| Heat distortion temperature | HDT | ISO 306 | 161 °C |
| 维卡软化温度，HDT |