Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO(PPE)+TPE NORYL™ WCP700 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC/NORYL™ WCP700 resin |
|---|---|---|---|
| Shore hardness | 邵氏A,30秒 | ASTM D2240 | 70 |
| film | Test Condition | Test Method | SABIC/NORYL™ WCP700 resin |
|---|---|---|---|
| Tear resistance of pants | ISO 6383-1 | 46.0 N/mm |
| Electrical performance | Test Condition | Test Method | SABIC/NORYL™ WCP700 resin |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 2.40 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| relative permittivity | 50Hz | IEC 60250 | 2.40 |
| Volume resistivity | IEC 60093 | 1.7E+16 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 2.40 |
| Dissipation Factor | 50Hz | IEC 60250 | 0.037 |
| 60Hz | IEC 60250 | 0.037 | |
| 1MHz | IEC 60250 | 5.2E-04 | |
| dielectric strength | 2.00mm,在油中 | IEC 60243-1 | 26 kV/mm |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL™ WCP700 resin |
|---|---|---|---|
| fracture | ISO 527-2/50 | 4.00 MPa | |
| ISO 527-2/50 | >400 % | ||
| ASTM D638 | >400 % | ||
| ASTM D638 | 5.00 MPa |
| physical property | Test Condition | Test Method | SABIC/NORYL™ WCP700 resin |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 10 g/10min |
| Shrinkage rate | TD:24小时 | ASTM D955 | 0.33 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.050 % |
| density | ASTM D792 | 0.928 g/cm³ | |
| melt mass-flow rate | 210°C/5.0kg | ASTM D1238 | 17 g/10min |
| Shrinkage rate | MD:24小时 | ASTM D955 | 0.48 % |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL™ WCP700 resin |
|---|---|---|---|
| brittle temperature | ASTM D746 | <-40.0 °C |