PPS OFL-4036 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and electrical components
Flame retardant,High heat resistance,Filler: Glass fiber reinf,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/OFL-4036 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 25 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 11.8 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.30 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.7 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 3.40 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/OFL-4036 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 12000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 121 Mpa |
| Wear factor | Washer | ASTM D3702Modified | 52.5 10^-10in^5-min/ft-lb-hr |
| tensile strength | 断裂 | ASTM D638 | 124 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 11600 Mpa |
| Tensile modulus | ASTM D638 | 12800 Mpa | |
| elongation | 断裂 | ASTM D638 | 1.3 % |
| coefficient of friction | Static | ASTM D3702Modified | 0.35 |
| bending strength | ISO 178 | 180 Mpa | |
| Flexural modulus | ISO 178 | 11100 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 1.3 % |
| Wear factor | Ring | ASTM D3702Modified | 7.00to8.00 10^-10in^5-min/ft-lb-hr |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.44 |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 178 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/OFL-4036 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.13-0.18 % |
| MD：24小时 | ASTM D955 | 0.10-0.20 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 1.2E-03 % |
| 平衡,23°C,50%RH | ISO 62 | 0.010 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.60-0.80 % |
| TD:24小时 | ISO 294-4 | 0.30-0.48 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/OFL-4036 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 278 °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 2.5E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 4.9E-05 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 5E-05 cm/cm/°C | |
| TD：-30to30°C | ASTM D696 | 3.4E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 278 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 2.3E-5to5.0E-5 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 2.4E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 257 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 264 °C |