PA612 FE3734 NC010 DUPONT USA
Zytel®
Engineering accessories、Automotive Applications、Engine parts
Mineral reinforcement、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/FE3734 NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| hardness | Test Condition | Test Method | DUPONT USA/FE3734 NC010 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 114 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/FE3734 NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| ASTM D412/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | ||
| Nominal tensile fracture strain | ISO 527-2 | 38 % | |
| elongation at break | ASTM D412/ISO 527 | 38 % | |
| Flexural modulus | ASTM D790/ISO 178 | 2200 kg/cm²(MPa)[Lb/in²] | |
| ISO 178 | 2200 Mpa | ||
| Tensile strain | 屈服 | ISO 527-2 | 13 % |
| tensile strength | ASTM D412/ISO 527 | 59 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | NB kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | 屈服 | ISO 527-2 | 59.0 Mpa |
| Rockwell hardness | ASTM D785 | R-114 |
| other | Test Condition | Test Method | DUPONT USA/FE3734 NC010 |
|---|---|---|---|
| characteristic | PA612.无筋.润滑 |
| Physical properties | Test Condition | Test Method | DUPONT USA/FE3734 NC010 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.3-1.4 % | |
| density | ASTM D792/ISO 1183 | 1.07 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.3 % |
| flammability | Test Condition | Test Method | DUPONT USA/FE3734 NC010 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/FE3734 NC010 |
|---|---|---|---|
| Shrinkage rate | TD：3.20mm | 1.1 % | |
| TD | ISO 294-4 | 1.4 % | |
| MD | ISO 294-4 | 1.3 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 3.0 % |
| viscosity number | 96%H2SO4 | ISO 307 | 95.0 cm³/g |
| Shrinkage rate | MD：3.20mm | 1.1 % | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.3 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/FE3734 NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 218 °C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 63 ℃（℉） |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 63.0 °C | |
| melting temperature | 218 ℃（℉） |