PC+ABS TAROBLEND 65 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTaro Plast S.p.A./TAROBLEND 65
Charpy Notched Impact Strength23°CISO 17930 kJ/m²
Impact strength of cantilever beam gap23°C,3.20mmASTMD256550 J/m
Impact strength of simply supported beam without notch23°CISO 179无断裂
Mechanical propertiesTest ConditionTest MethodTaro Plast S.p.A./TAROBLEND 65
Flexural modulusASTMD7902150 MPa
elongation断裂ASTMD63850 %
bending strength断裂ASTM D79080.0 MPa
Tensile modulusASTMD6382100 MPa
bending strength--ISO 17880.0 MPa
tensile strength 屈服ASTMD63850.0 MPa
Electrical performanceTest ConditionTest MethodTaro Plast S.p.A./TAROBLEND 65
Volume resistivityASTM D257>1.0E+15 ohms·cm
dielectric strength2.00mmASTM D14924 kV/mm
Compared to the Leakage Tracking Index (CTI)解决方案AIEC 60112PLC 2
flammabilityTest ConditionTest MethodTaro Plast S.p.A./TAROBLEND 65
burning rateFMVSS302<100 mm/min
UL flame retardant rating1.6mmUL 94HB
Limiting Oxygen IndexASTM D286323 %
physical property Test ConditionTest MethodTaro Plast S.p.A./TAROBLEND 65
Shrinkage rateMDASTM D9550.40to0.70 %
densityASTMD7921.13to1.15 g/cm³
Water absorption rate23°C,24hrASTMD5700.20 %
Shrinkage rateTDASTM D9550.40to0.70 %
melt mass-flow rate260°C/5.0kgASTMD123812 g/10min
Water absorption rate饱和,23°CASTMD5700.60 %
Thermal performanceTest ConditionTest MethodTaro Plast S.p.A./TAROBLEND 65
Heat distortion temperature1.8MPa,未退火，HDTASTMD648118 °C
vicat--ASTMD15254130 °C
ball-indentation hardness125°CVDE0470通过
Linear coefficient of thermal expansionMD：-30到30°CASTM D6966.5E-05 cm/cm/°C
Continuous use temperatureIEC 6021690.0 °C
vicat--ASTMD15255125 °C