density

ASTMD792

g/cm³

1

density

ASTMD792

g/cm³

1

Melt mass flow rate

300°C/1.2kg

ASTMD1238

g/10min

1

Shrinkage rate

MD：3.20mm

内部方法

%

0

Specific volume

ASTMD792

cm³/g

0

Water absorption rate

24hr

ASTMD570

%

0

Water absorption rate

平衡,23°C

ASTMD570

%

0

Water absorption rate

平衡,100°C

ASTMD570

%

0

Impact strength of simply supported beam gap

-30°C

ISO179/1eA

kJ/m²

1

Impact strength of simply supported beam gap

23°C

ISO179/1eA

kJ/m²

6

Tensile impact strength

ASTMD1822

kJ/m²

5

tensile strength

屈服

ASTMD638

Mpa

6

tensile strength

断裂

ASTMD638

Mpa

6

Falling hammer impact

23°C

ASTMD3029

J

1

elongation

断裂

ASTMD638

%

1

elongation

屈服

ASTMD638

%

7

Taber abraser

1000Cycles,1000g,CS-17转轮

ASTMD1044

mg

1

Bending modulus

50.0mm跨距

ASTMD790

Mpa

2

bending strength

屈服,50.0mm跨距

ASTMD790

Mpa

9

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

6

Suspended wall beam gap impact strength

-30°C

ISO180/1A

kJ/m²

1

Suspended wall beam gap impact strength

23°C

ISO180/1A

kJ/m²

6

Impact strength of cantilever beam gap

23°C

ASTMD4812

J/m

3

Dart impact equipped with measuring instruments

23°C,EnergyatPeakLoad

ASTMD3763

J

6

RTI Imp

UL746

°C

1

RTIElec

UL746

°C

1

RTIStr

UL746

°C

1

specific heat

ASTMC351

J/kg/°C

1

thermal conductivity

ASTMC177

W/m/K

0

Hot deformation temperature

0.45MPa,未退火,6.40mm

ASTMD648

°C

1

Hot deformation temperature

1.8MPa,未退火,6.40mm

ASTMD648

°C

1

vicat softening point

ASTMD15257

°C

1

Linear coefficient of thermal expansion

MD：-40到95°C

ASTME831

cm/cm/°C

6

Dielectric strength

3.20mm,inAir

ASTMD149

KV/mm

1

Volume resistivity

ASTMD257

ohms·cm

>

Light transmittance

2540µm

ASTMD1003

%

8

Haze

2540µm

ASTMD1003

%

1