Certificates
PA66 CM3004G20 TORAY SHENZHEN
Amilan®
Office supplies、Automotive sector、building materials、Electronic field、Electrical field
Flame retardant、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TORAY SHENZHEN/CM3004G20 |
|---|---|---|---|
| bending strength | -，23℃ | D790 | 210 Mpa |
| abrasion | D1044 | 25 mg/1000 | |
| elongation at break | 23℃ | D638 | 5 % |
| Flexural modulus | 23℃ | D790 | 7.0 GPa |
| Impact Strength | -，23℃ | D256 | 50 kJ/m² |
| tensile yield strength | -，23℃ | D638 | 130 Mpa |
| Impact Strength | -，23℃ | D256 | 80 J/m |
| Electrical performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G20 |
|---|---|---|---|
| Volume resistivity | D257 | 1013 Ω.m | |
| Dielectric insulation strength | D149 | 31 MV/m |
| processability | Test Condition | Test Method | TORAY SHENZHEN/CM3004G20 |
|---|---|---|---|
| Shrinkage rate | -，3mmt | 0.8-1.2 % | |
| -，1mmt | 0.4-0.6 % |
| physical property | Test Condition | Test Method | TORAY SHENZHEN/CM3004G20 |
|---|---|---|---|
| Filling content | 20 wt% | ||
| Rockwell hardness | 23℃ | D785 | 150 R |
| Water absorption rate | -，23℃,24hrs | D570 | 0.4 % |
| -，23℃,水中 | D570 | 4.5 % |
| Thermal performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G20 |
|---|---|---|---|
| melting point | DSC | 265 °C | |
| Flame retardancy | UL94 | V-0 |