Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 G3300 L INVISTA USA
TORZEN®
--
Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | INVISTA USA/G3300 L |
|---|---|---|---|
| Charpy Notched Impact Strength | -40℃ | ISO 179 | 10 kJ/m² |
| Tensile modulus | ISO 527-2 | 10500 Mpa | |
| tensile strength | 断裂 | ISO 527 | 205 Mpa |
| bending strength | ISO 178 | 285 Mpa | |
| Flexural modulus | ISO 178 | 9500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.1 % |
| tensile strength | 断裂 | ISO 527-2 | 205 Mpa |
| elongation at break | ISO 527 | 3.1 % | |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 12 kJ/m² |
| Tensile modulus | ISO 527 | 10500 Mpa | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180 | 12 kJ/m² |
| physical property | Test Condition | Test Method | INVISTA USA/G3300 L |
|---|---|---|---|
| Glass Fiber Content | ISO 3451/4 | 33 % | |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.30-0.40 % |
| 正常: 2.00 mm | ISO 294-4 | 0.90 - 1.10 % | |
| 平行: 2.00 mm | ISO 294-4 | 0.30- 0.40 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.2 % |
| 23℃, 24 hr | ISO 62 | 1.2 % | |
| 平衡,23°C,50%RH | ISO 62 | 1.8 % | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.90-1.1 % |
| Water absorption rate | 平衡, 23℃, 50% RH | ISO 62 | 1.8 % |
| Thermal performance | Test Condition | Test Method | INVISTA USA/G3300 L |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75 | 255 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 255 °C | |
| melting temperature | 10℃/min | ISO 11357 | 262 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 248 °C |
| 1.82 MPa, 未退火，HDT | ISO 75 | 248 °C |