PEI AUT200-GY8D115 SABIC INNOVATIVE SHANGHAI
ULTEM™ Resin
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/AUT200-GY8D115 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 1300 J/m |
| 23°C7 | ISO 180/1U | 无断裂 | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 33.0 J |
| Suspended wall beam without notch impact strength | -30°C7 | ISO 180/1U | 无断裂 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/AUT200-GY8D115 |
|---|---|---|---|
| Tensile modulus | --1 | ASTM D638 | 3590 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 85.0 Mpa |
| 屈服2 | ASTM D638 | 110 Mpa | |
| elongation | 断裂2 | ASTM D638 | 60 % |
| Flexural modulus | --4 | ISO 178 | 3300 Mpa |
| bending strength | 屈服, 50.0 mm 跨距3 | ASTM D790 | 165 Mpa |
| --4,5 | ISO 178 | 160 Mpa | |
| elongation | 屈服 | ISO 527-2/5 | 6.0 % |
| Flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 3520 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 105 Mpa |
| elongation | 屈服2 | ASTM D638 | 7.0 % |
| tensile strength | 断裂2 | ASTM D638 | 105 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 3200 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 60 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/AUT200-GY8D115 |
|---|---|---|---|
| Melt volume flow rate | 360°C/5.0 kg | ISO 1133 | 25.0 cm3/10min |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.70 % |
| melt mass-flow rate | 337°C/6.7 kg | ASTM D1238 | 18 g/10 min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 1.3 % |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/AUT200-GY8D115 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距7，HDT | ISO 75-2/Af | 193 °C |
| vicat | -- | ASTM D15259 | 219 °C |
| Metallic haze | 起始 | 内部方法 | 204 °C |
| Linear coefficient of thermal expansion | 流动 : 23 到 150°C | ISO 11359-2 | 5.0E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 205 °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距8，HDT | ISO 75-2/Ae | 190 °C | |
| vicat | -- | ISO 306/B120 | 212 °C |
| Linear coefficient of thermal expansion | 横向 : -40 到 150°C | ASTM E831 | 5.5E-5 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 211 °C |
| Linear coefficient of thermal expansion | 流动 : -40 到 150°C | ASTM E831 | 5.5E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 199 °C |
| Linear coefficient of thermal expansion | 横向 : 23 到 150°C | ISO 11359-2 | 5.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 197 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/AUT200-GY8D115 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 350 to 400 °C | ||
| drying temperature | 150 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 4.0 to 6.0 hr | ||
| Temperature in the middle of the barrel | 340 to 400 °C | ||
| Temperature at the rear of the barrel | 330 to 400 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 345 to 400 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 135 to 165 °C | ||
| Spray nozzle temperature | 345 to 400 °C |