Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT V2000DM SABIC INNOVATIVE NANSHA
VALOX™
Home appliance components、Automotive Applications
High rigidity、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V2000DM |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ASTM D4812 | NoBreak |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 54.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 2.0 kJ/m² |
| 23°C | ISO 180/1A | 5.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V2000DM |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3000 Mpa | |
| elongation | 屈服 | ASTM D638 | 20 % |
| tensile strength | 断裂 | ASTM D638 | 40.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 7.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 55.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2570 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 59.0 Mpa |
| Tensile modulus | ASTM D638 | 2810 Mpa | |
| elongation | 断裂 | ASTM D638 | 100 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 90.0 Mpa |
| Flexural modulus | ISO 178 | 2500 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 59.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 15 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V2000DM |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 35 g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 2.1-2.4 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.34 % |
| 饱和,23°C | ISO 62 | 0.080 % | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 34.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V2000DM |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 185 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 8.4E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 186 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 8.4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 53.0 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 54.0 °C | |
| vicat | ASTM D15259 | 185 °C |