Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM M270-44 WK2001 DAICEL MALAYSIA
DURACON®
Fitness equipment、Automotive Applications
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDAICEL MALAYSIA/M270-44 WK2001
Charpy Notched Impact Strength23°CISO179/1eA5.3 kJ/m²
Supplementary InformationTest ConditionTest MethodDAICEL MALAYSIA/M270-44 WK2001
ColorNumberCF2001/CD3068
hardnessTest ConditionTest MethodDAICEL MALAYSIA/M270-44 WK2001
Rockwell hardnessM级ISO2039-280
Electrical performanceTest ConditionTest MethodDAICEL MALAYSIA/M270-44 WK2001
Surface ResistivityIEC600931E+16 ohms
Volume resistivityIEC600931E+14 ohms·cm
dielectric strength3.00mmIEC60243-119 KV/mm
Mechanical propertiesTest ConditionTest MethodDAICEL MALAYSIA/M270-44 WK2001
Wear factor0.98MPa,0.30m/sec4JISK7218<1.0 10^-8mm³/N·m
Nominal tensile fracture strainISO527-230 %
Wear factor0.98MPa,0.30m/sec5JISK721830 10^-8mm³/N·m
Tensile stressISO527-263.0 Mpa
Dynamic2JISK72180.37
Bending stressISO17888.0 Mpa
与钢-动态3JISK72180.40
Tensile modulusISO527-22800 Mpa
Flexural modulusISO1782550 Mpa
flammabilityTest ConditionTest MethodDAICEL MALAYSIA/M270-44 WK2001
UL flame retardant ratingUL94HB
physical property Test ConditionTest MethodDAICEL MALAYSIA/M270-44 WK2001
Shrinkage rateMD:2.00mmISO294-41.9 %
melt mass-flow rateISO113327 g/10min
Shrinkage rateTD:2.00mmISO294-41.9 %
Melt volume flow rate190°C/2.16kgISO113323.0 cm3/10min
Water absorption rate23°C,24hrISO620.50 %
densityISO11831.41 g/cm³
melt mass-flow rateASTMD123827 g/10min
Thermal performanceTest ConditionTest MethodDAICEL MALAYSIA/M270-44 WK2001
1.8MPa,未退火ISO75-2/A100 °C
MD：23到55°C内部方法1.1E-04 cm/cm/°C
TD：23to55°C内部方法1.1E-04 cm/cm/°C