Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PC/PET HX7509HP SABIC INNOVATIVE US
XYLEX™
Automotive Applications、Electronic and electrical
Flame retardant、High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 77.0 J |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
---|---|---|---|
bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 95.0 Mpa |
tensile strength | 屈服4 | ASTM D638 | 60.0 Mpa |
elongation | 断裂4 | ASTM D638 | 140 % |
Tensile modulus | --3 | ASTM D638 | 2150 Mpa |
elongation | 断裂 | ISO 527-2/50 | 130 % |
Flexural modulus | 50.0mm跨距5 | ASTM D790 | 2300 Mpa |
bending strength | --6,7 | ISO 178 | 92.0 Mpa |
Flexural modulus | --6 | ISO 178 | 2260 Mpa |
tensile strength | 断裂 | ISO 527-2/50 | 62.0 Mpa |
屈服 | ISO 527-2/50 | 60.0 Mpa | |
elongation | 屈服 | ISO 527-2/50 | 5.8 % |
屈服4 | ASTM D638 | 6.3 % | |
tensile strength | 断裂4 | ASTM D638 | 63.0 Mpa |
Tensile modulus | -- | ISO 527-2/1 | 2300 Mpa |
optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
---|---|---|---|
Haze ratio | 2540µm | ASTM D1003 | 2.0 % |
transmissivity | 2540µm | ASTM D1003 | 88.0 % |
flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
---|---|---|---|
UL flame retardant rating | 0.75mm | UL 94 | V-2 |
physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.40-0.60 % |
melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 12 g/10min |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
饱和,23°C | ISO 62 | 0.12 % | |
Shrinkage rate | TD:3.20mm | 内部方法 | 0.50-0.70 % |
Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 11.5 cm3/10min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HX7509HP |
---|---|---|---|
thermal conductivity | ISO 8302 | 0.23 W/m/K | |
Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 6.8E-05 cm/cm/°C |
TD:-40到40°C | ASTME831 | 1E-04 cm/cm/°C | |
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 119 °C |
vicat | -- | ISO 306/B50 | 125 °C |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 106 °C |
1.8MPa,未退火,64.0mm跨距10,HDT | ISO 75-2/Af | 108 °C | |
vicat | -- | ASTM D-596 | 126 °C |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
TD:-40到40°C | ISO 11359-2 | 6.8E-05 cm/cm/°C |