Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MVLDPE 2036P STYRON US
DOWLEX™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | STYRON US/2036P |
|---|---|---|---|
| Film toughness | 25.4um，TD | ASTM D-882 | 308 J/cm4 |
| Thin film puncture strength | 25.4um | 内部方法 | 10.3 J/cm³ |
| Film toughness | 25.4um，MD | ASTM D-882 | 324 J/cm³ |
| film | Test Condition | Test Method | STYRON US/2036P |
|---|---|---|---|
| Thin film puncture strength | 25µm | 内部方法 | 10.3 J/cm³ |
| elongation | TD:断裂,25µm | ASTM D882 | 750 % |
| Elmendorf tear strength | TD:25µm | ASTM D1922 | 290 g |
| Dart impact | 25µm | ASTM D1709A | 57 g |
| tensile strength | TD:屈服,25µm | ASTM D882 | 17.6 Mpa |
| TD:断裂,25µm | ASTM D882 | 39.9 Mpa | |
| film strength | TD:25µm | ASTM D882 | 308 J/cm³ |
| elongation | MD:断裂,25µm | ASTM D882 | 620 % |
| tensile strength | MD:屈服,25µm | ASTM D882 | 16.9 Mpa |
| MD:断裂,25µm | ASTM D882 | 59.2 Mpa | |
| film thickness | 25 µm | ||
| Elmendorf tear strength | MD:25µm | ASTM D1922 | 83 g |
| film strength | MD:25µm | ASTM D882 | 324 J/cm³ |
| Basic performance | Test Condition | Test Method | STYRON US/2036P |
|---|---|---|---|
| film thickness | 25.4 um | ||
| density | ASTM D-792 | 0.935 g/m3 | |
| melt mass-flow rate | ASTM D-1238 | 2.5 g/10min |
| Mechanical properties | Test Condition | Test Method | STYRON US/2036P |
|---|---|---|---|
| Dart impact | 25.4um | ASTM D-1709A | 57 g |
| tensile strength | 25.4um，屈服,MD | ASTM D-882 | 16.9 Mpa |
| elongation at break | 25.4um，MD | ASTM D-882 | 620 % |
| tensile strength | 25.4um，TD,断裂 | ASTM D-882 | 39.9 Mpa |
| Elmendorf tear strength | 25.4um，MD | ASTM D-1922 | 83 g |
| elongation at break | 25.4um，TD | ASTM D-882 | 750 % |
| tensile strength | 25.4um，MD,断裂 | ASTM D-882 | 59.2 Mpa |
| Elmendorf tear strength | 25.4um，TD | ASTM D-1922 | 290 g |
| optical performance | Test Condition | Test Method | STYRON US/2036P |
|---|---|---|---|
| gloss | 45°，25.4um | ASTM D-2457 | 90 |
| 45°,25.4µm | ASTM D2457 | 90 | |
| Haze ratio | 25.4µm | ASTM D1003 | 2.6 % |
| 25.4um | ASTM D-1003 | 2.6 % |
| processability | Test Condition | Test Method | STYRON US/2036P |
|---|---|---|---|
| Melt Temperature | 274 °C |
| physical property | Test Condition | Test Method | STYRON US/2036P |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 2.5 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/2036P |
|---|---|---|---|
| vicat | ASTM D1525 | 119 °C | |
| melting temperature | 内部方法 | 125 °C | |
| vicat | ASTM D-1525 | 119 °C |