LDPE Polymer-E H0105 Asia Polymer Corporation (APC)
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E H0105 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 54 |
| film | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E H0105 |
|---|---|---|---|
| tensile strength | TD:断裂,32µm,吹塑薄膜 | ASTM D882 | 21.6 MPa |
| Dart impact | 32µm,吹塑薄膜 | ASTM D1709 | 300 g |
| Secant modulus | 1%正割,TD:32µm,吹塑薄膜 | ASTM D882 | 216 MPa |
| elongation | TD:断裂,32µm,吹塑薄膜 | ASTM D882 | 500 % |
| Elmendorf tear strength | MD:31.8µm | ASTM D1922 | 51.0 kN/m |
| tensile strength | MD:断裂,32µm,吹塑薄膜 | ASTM D882 | 25.5 MPa |
| elongation | MD:断裂,32µm,吹塑薄膜 | ASTM D882 | 330 % |
| Elmendorf tear strength | TD:31.8µm | ASTM D1922 | 73.5 kN/m |
| Secant modulus | 1%正割,MD:32µm,吹塑薄膜 | ASTM D882 | 196 MPa |
| Mechanical properties | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E H0105 |
|---|---|---|---|
| coefficient of friction | ASTM D1894 | <0.55 |
| optical performance | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E H0105 |
|---|---|---|---|
| gloss | 60°,31.8µm,吹塑薄膜 | ASTM D523 | 75 |
| Haze ratio | 31.8µm,吹塑薄膜 | ASTM D1003 | 10 % |
| physical property | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E H0105 |
|---|---|---|---|
| density | ASTM D1505 | 0.923 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.50 g/10min |
| Thermal performance | Test Condition | Test Method | Asia Polymer Corporation (APC)/Polymer-E H0105 |
|---|---|---|---|
| vicat | ASTM D1525 | 101 °C | |
| melting temperature | 内部方法 | 108 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 52.0 °C |
| brittle temperature | ASTM D746 | <-70.0 °C |