Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RN001S SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical applications,Home appliance components
Thermal stability,UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RN001S |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 223 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 301 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 76.7 °C | |
| 0.45MPa,未退火,3.20mm | ASTM D648 | 231 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RN001S |
|---|---|---|---|
| Bending modulus | ASTM D790 | 3450 Mpa | |
| ISO 178 | 3400 Mpa | ||
| bending strength | ISO 178 | 107 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.8 % |
| 屈服 | ASTM D638 | 2.9 % | |
| Friction coefficient | Dynamic | ASTM D3702Modified | 0.75 |
| Static | ASTM D3702Modified | 0.55 | |
| Tensile modulus | ASTM D638 | 4140 Mpa | |
| ISO 527-2/1 | 3910 Mpa | ||
| Tensile strain | 屈服 | ISO 527-2 | 2.1 % |
| 断裂 | ISO 527-2 | 42 % | |
| tensile strength | 屈服 | ASTM D638 | 84.1 Mpa |
| 屈服 | ISO 527-2 | 69.0 Mpa | |
| 断裂 | ASTM D638 | 84.1 Mpa | |
| 断裂 | ISO 527-2 | 69.0 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 103 10^-10in^5-min/ft-lb-hr |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RN001S |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ISO 294-4 | 1.0 % |
| MD:24小时 | ISO 294-4 | 1.0 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/RN001S |
|---|---|---|---|
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 2.30 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 2.8 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 54 kJ/m² |