Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML7672-111 SABIC EU
LEXAN™
Electronic and electrical、Automotive components、Casters
High temperature resistan、Flame retardant、Filler: Glass fiber reinf
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC EU/ML7672-111 |
|---|---|---|---|
| 23°C | ISO 180/1A | 19 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 19 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 28.2 J |
| 23°C | ASTM D256 | 240 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC EU/ML7672-111 |
|---|---|---|---|
| fracture | ISO 527-2/5 | 57.0 Mpa | |
| ASTM D638 | 5.0 % | ||
| --6 | ISO 178 | 100 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 99.0 Mpa | |
| --5 | ISO 178 | 5480 Mpa | |
| yield | ISO 527-2/5 | 11.0 Mpa | |
| ISO 527-2/5 | 0.30 % | ||
| 50.0mm span | ASTM D790 | 4860 Mpa | |
| fracture | ASTM D638 | 52.0 Mpa | |
| ISO 527-2/5 | 1.8 % | ||
| --1 | ASTM D638 | 5200 Mpa |
| physical property | Test Condition | Test Method | SABIC EU/ML7672-111 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.60 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 5.00 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.30 % |
| 饱和,23°C | ISO 62 | 0.20 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 4.5 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC EU/ML7672-111 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6.9E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 140 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 138 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 2.7E-05 cm/cm/°C |