| Thermal Properties | Test Condition | Test Method | TAIWAN CHIMEI/PC-365 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 115 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 127 °C |
| Linear thermal expansion coefficient | MD：23到55°C | ISO11359-2 | 8E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ASTMD152511 | 125 °C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 106 °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 138 °C |
| -- | ASTMD152510 | 136 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 102 °C |
| Hardness | Test Condition | Test Method | TAIWAN CHIMEI/PC-365 |
|---|---|---|---|
| Rockwell Hardness | R计秤,23°C | ASTMD785 | 115 |
| R计秤,23°C | ISO2039-2 | 115 |
| Mechanical Properties | Test Condition | Test Method | TAIWAN CHIMEI/PC-365 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2200 Mpa | |
| Flexural Strength | 23°C | ASTMD790 | 78.5 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 50.0 Mpa |
| Tensile Strain | Break,23°C | ASTMD638 | 85 % |
| Flexural Modulus | 23°C | ASTMD790 | 2260 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 54.0 Mpa |
| Tensile Strain | 断裂 | ISO527-2/50 | 120 % |
| Tensile Strength | Yield,23°C | ASTMD638 | 53.0 Mpa |
| Flexural Stress | ISO178 | 80.0 Mpa |
| Physical | Test Condition | Test Method | TAIWAN CHIMEI/PC-365 |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/5.0kg | ISO1133 | 20 g/10min |
| 内部方法 | 30.0 CM | ||
| Density / Specific Gravity | 23°C | ISO1183 | 1.13 g/cm³ |
| Modeling Shrinkage | ISO2577 | 0.40to0.60 % | |
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 20 g/10min |
| Density/Specific Gravity 2 | ASTMD792 | 1.13 g/cm³ | |
| Modeling Shrinkage | MD | ASTMD955 | 0.40to0.60 % |
| Impact Properties | Test Condition | Test Method | TAIWAN CHIMEI/PC-365 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180 | 45 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 50 kJ/m² |
| Notched Izod Impact Strength | -30°C,3.18mm | ASTMD256 | 490 J/m |
| 23°C,3.18mm | ASTMD256 | 540 J/m | |
| 23°C | ISO180 | 50 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 45 kJ/m² |
| Flammability | Test Condition | Test Method | TAIWAN CHIMEI/PC-365 |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | TAIWAN CHIMEI/PC-365 |
|---|---|---|---|
| Volume Resistivity | IEC60093 | 1E+18 ohms·cm | |
| Dielectric Constant | 1MHz | IEC60250 | 3.10 |
| Surface Resistivity | IEC60093 | 1E+16 ohms |