Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3WG7 BK00564 BASF SHANGHAI
Ultramid®
Automotive sector、Shell、Engine parts、Industrial applications
Oil resistant、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | BASF SHANGHAI/A3WG7 BK00564 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 28 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/A3WG7 BK00564 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 12 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 10000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 11500 Mpa |
| elongation at break | 23°C | ISO 527-2 | 2.5 % |
| tensile strength | 23°C | ISO 527-2 | 200 Mpa |
| Flame retardant performance | Test Condition | Test Method | BASF SHANGHAI/A3WG7 BK00564 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 0.71mm | |
| UL -94 | HB 1.50mm | ||
| UL -94 | HB 3.00mm |
| physical property | Test Condition | Test Method | BASF SHANGHAI/A3WG7 BK00564 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 5.0 % |
| density | ISO 1183 | 1.41 g/cm³ | |
| Water absorption rate | (23°C,50RH) | ISO 62 | 1.6 % |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/A3WG7 BK00564 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 250 °C |