PA612 612GF30 H9 A SCHULMAN USA
SCHULAMID®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/612GF30 H9 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23℃ | J/m | 0.105to0.332 |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/612GF30 H9 |
|---|---|---|---|
| Yield, 23 ℃ | % | 2.0to2.5 | |
| Flexural modulus | 23℃ | 5510.34to22413.79 MPa | |
| tensile strength | 23℃ | 123.45to207.59 MPa | |
| Tensile modulus | 23℃ | 6551.72to27586.21 MPa | |
| Fracture, 23 ℃ | % | 1.0to2.3 | |
| bending strength | 23℃ | 188.28to334.48 MPa |
| Electrical performance | Test Condition | Test Method | A SCHULMAN USA/612GF30 H9 |
|---|---|---|---|
| Volume resistivity | 23℃ | ohms·cm | 1.0-2.5E+4 |
| physical property | Test Condition | Test Method | A SCHULMAN USA/612GF30 H9 |
|---|---|---|---|
| Shrinkage rate | MD：23℃ | mm/mm | 25.4E-3-76.2E-3 |
| Water absorption rate | 23℃,24hr | % | 0.10to0.20 |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/612GF30 H9 |
|---|---|---|---|
| 0.45MPa, Not annealed | °C | 210to221 | |
| 1.8MPa, Not annealed | °C | 197to218 |