| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® MB8900 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 30 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® MB8900 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 44 % | |
| Tensile modulus | ISO 527-2 | 2800 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 3.5 % |
| tensile strength | 屈服 | ISO 527-2 | 55.0 MPa |
| Flexural modulus | ISO 178 | 2600 MPa | |
| bending strength | ISO 178 | 88.0 MPa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® MB8900 |
|---|---|---|---|
| UL flame retardant rating | 1.00mm | UL 94 | V-1 |
| 1.50mm | UL 94 | 5VB |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® MB8900 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.25to0.45 % | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 23.0 cm³/10min |
| Shrinkage rate | 吸水率(饱和,23°C) | 0.20 % | |
| MD:3.20mm | 0.25to0.45 % | ||
| density | ISO 1183 | 1.20 g/cm³ | |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 25 g/10min |