POP 8102L SABIC INNOVATIVE KOREA
SABIC® COHERE™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC INNOVATIVE KOREA/8102L |
|---|---|---|---|
| 邵氏 A, 1 秒 | ASTM D2240 | 92 | |
| 邵氏 D, 1 秒 | ASTM D2240 | 40 |
| film | Test Condition | Test Method | SABIC INNOVATIVE KOREA/8102L |
|---|---|---|---|
| Tangent modulus 3 | 1% 正割, TD : 50 µm, 吹塑薄膜 | ASTM D882 | 76.0 Mpa |
| Elongation rate 3 | TD : 断裂, 50 µm, 吹塑薄膜 | ASTM D882 | 620 % |
| Tangent modulus 3 | 1% 正割, MD : 50 µm, 吹塑薄膜 | ASTM D882 | 68.0 Mpa |
| Falling hammer impact | 50 µm, 吹塑薄膜 | ASTM D1709 | > 1000 g |
| Tensile strength 3 | MD : 断裂, 50 µm, 吹塑薄膜 | ASTM D882 | 47.0 Mpa |
| Elongation rate 3 | MD : 断裂, 50 µm, 吹塑薄膜 | ASTM D882 | 600 % |
| Tensile strength 3 | TD : 断裂, 50 µm, 吹塑薄膜 | ASTM D882 | 42.0 Mpa |
| Elmendorf Tear Strength?4 | MD : 50.0 µm | ASTM D1922 | 10 g/µm |
| TD : 50.0 µm | ASTM D1922 | 17 g/µm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE KOREA/8102L |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 800 % |
| tensile strength | 断裂 | ASTM D638 | 24.5 Mpa |
| Bending modulus -1% secant | ASTM D790 | 82.4 Mpa | |
| Tear strength 2 | ASTM D624 | 8.53 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/8102L |
|---|---|---|---|
| Haze ratio | ASTM D1003 | 4.0 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE KOREA/8102L |
|---|---|---|---|
| Mooney viscosity | ML 1+4, 121°C | ASTM D1646 | 20 MU |