PA612 151L-WT928 PA612 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA612 DUPONT USA 151L-WT928

Injection grade

US$ 5,060 / MT

FOB Guangzhou port, China

Supplementary Information	Test Condition	Test Method	DUPONT USA/151L-WT928
EmissionofOrganicCompounds		VDA277	3.10 µgC/g
Odor		VDA270	4.50
flammability	Test Condition	Test Method	DUPONT USA/151L-WT928
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-2
UL flame retardant rating		0.9mm	UL 94	V-2
Extreme Oxygen Index		ISO 4589-2	27 %
UL flame retardant rating	0.9mm	IEC 60695-11-10,-20	V-2
UL flame retardant rating		1.5mm	UL 94	V-2
FMVSS flammability		FMVSS302	DNI
thermal performance	Test Condition	Test Method	DUPONT USA/151L-WT928
Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C
		MD：--	ISO 11359-2	1.1E-04 cm/cm/°C
		MD：55to160°C	ISO 11359-2	1.6E-04 cm/cm/°C
		TD：--	ISO 11359-2	1.2E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	135 °C
Glass transition temperature		ISO 11357-2	65.0 °C
Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.8E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	62.0 °C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C
Melting temperature		ISO 11357-3	218 °C
Vicat softening temperature		ISO 306/B50	181 °C
Physical properties	Test Condition	Test Method	DUPONT USA/151L-WT928
MediumDensity			0.900 g/cm³
Shrinkage rate	MD	ISO 294-4	1.3 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	3.0 %
Water absorption rate		Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.3 %
ThermalConductivityofMelt			0.18 W/m/K
Shrinkage rate	MD：3.20mm		1.1 %
SpecificHeatCapacity of Melt			2750 J/kg/°C
Stickiness	96%H2SO4	ISO 307	95.0 cm³/g
Shrinkage rate	TD：3.20mm		1.1 %
Shrinkage rate		TD	ISO 294-4	1.4 %
Electrical performance	Test Condition	Test Method	DUPONT USA/151L-WT928
Dissipation factor	100Hz	IEC 60250	0.014
Compared to the anti leakage trace index		IEC 60112	PLC 0
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	0.016
Relative permittivity	100Hz	IEC 60250	3.60
Surface resistivity		IEC 60093	-- ohms
Relative permittivity	1MHz	IEC 60250	3.20
Dielectric strength		IEC 60243-1	30 KV/mm
mechanical properties	Test Condition	Test Method	DUPONT USA/151L-WT928
Tensile modulus		ISO 527-2	2400 Mpa
Tensile strain	Yield	ISO 527-2	4.5 %
Nominal tensile fracture strain		ISO 527-2	17 %
tensile strength	Yield	ISO 527-2	62.0 Mpa
Bending modulus		ISO 178	2100 Mpa
impact performance	Test Condition	Test Method	DUPONT USA/151L-WT928
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	NoBreak
film	Test Condition	Test Method	DUPONT USA/151L-WT928
Tensile strain	Yield，MD	ISO 527-3	4.5 %
hardness	Test Condition	Test Method	DUPONT USA/151L-WT928
Rockwell hardness	R-Scale	ISO 2039-2	114