MMBS ZYLAR® 670 INEOS Barex
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INEOS Barex/ZYLAR® 670 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 110 J/m |
| Dart impact | ASTM D5420 | 7.91 J | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 130 kJ/m² |
| Suspended wall beam without notch impact strength | ISO 180 | 140 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 6.0 kJ/m² |
| hardness | Test Condition | Test Method | INEOS Barex/ZYLAR® 670 |
|---|---|---|---|
| Rockwell hardness | M级 | 70 | |
| M级 | ASTM D785 | 70 |
| Mechanical properties | Test Condition | Test Method | INEOS Barex/ZYLAR® 670 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 42 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 42 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 28.0 MPa |
| Flexural modulus | ASTM D790 | 1830 MPa | |
| Tensile modulus | ASTM D638 | 1830 MPa | |
| ISO 527-2 | 1800 MPa | ||
| Flexural modulus | ISO 178 | 1800 MPa | |
| bending strength | ASTM D790 | 41.4 MPa | |
| ISO 178 | 41.0 MPa | ||
| tensile strength | 屈服,23°C | ASTM D638 | 27.6 MPa |
| Electrical performance | Test Condition | Test Method | INEOS Barex/ZYLAR® 670 |
|---|---|---|---|
| dielectric constant | 100Hz | IEC 60250 | 2.50 |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | >1.0E+14 ohms |
| optical performance | Test Condition | Test Method | INEOS Barex/ZYLAR® 670 |
|---|---|---|---|
| transmissivity | 550nm | ASTM D1003 | 91.0 % |
| refractive index | ASTM D542 | 1.560 | |
| Haze ratio | ASTM D1003 | 2.0 % | |
| refractive index | ISO 489 | 1.560 |
| physical property | Test Condition | Test Method | INEOS Barex/ZYLAR® 670 |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 55.0 cm³/10min |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 6.0 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.20to0.60 % |
| Water absorption rate | 饱和,23°C | ASTM D570 | 0.10 % |
| Shrinkage rate | ISO 294-4 | 0.20to0.60 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| 饱和,23°C | ISO 62 | 0.10 % | |
| density | ASTM D792 | 1.05 g/cm³ | |
| ISO 1183 | 1.05 g/cm³ | ||
| Melt volume flow rate | 200°C/5.0kg | ISO 1133 | 6.00 cm³/10min |
| Thermal performance | Test Condition | Test Method | INEOS Barex/ZYLAR® 670 |
|---|---|---|---|
| vicat | ISO 306/B50 | 72.0 °C | |
| ASTM D15252 | 97.8 °C | ||
| maximum service temperature | 250 °C |