ABS FR15U-NA1000 SABIC INNOVATIVE US
CYCOLAC™
small home appliances、Automotive sector、Electronic field、Electrical field
Flame retardant、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U-NA1000 |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 28.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U-NA1000 |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2060 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 41.0 Mpa |
| 屈服3 | ASTM D638 | 37.0 Mpa | |
| elongation | 断裂3 | ASTM D638 | 17 % |
| 屈服3 | ASTM D638 | 2.4 % | |
| 断裂 | ISO 527-2/50 | 22 % | |
| Flexural modulus | --5 | ISO 178 | 2260 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 67.0 Mpa |
| --5,6 | ISO 178 | 63.0 Mpa | |
| tensile strength | 断裂3 | ASTM D638 | 30.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2210 Mpa |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2340 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U-NA1000 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | > 1.0E+14 ohms·cm | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| arc resistance | ASTM D495 | PLC 7 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 20 KV/mm |
| High arc combustion index (HAI) | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U-NA1000 |
|---|---|---|---|
| UL flame retardant rating | 2.8 mm | UL 94 | 5VA |
| 1.5 mm | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U-NA1000 |
|---|---|---|---|
| melt viscosity | 200°C, 1000 sec^-1 | ASTM D3835 | 320 Pa·s |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U-NA1000 |
|---|---|---|---|
| melt mass-flow rate | 230°C/3.8 kg | ASTM D1238 | 3.3 g/10 min |
| 220°C/5.0 kg | ISO 1133 | 7.0 g/10 min | |
| Melt volume flow rate | 220°C/10.0 kg | ISO 1133 | 40.0 cm3/10min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U-NA1000 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 9.0E-5 cm/cm/°C |
| vicat | -- | ASTM D15258 | 93.0 °C |
| -- | ISO 306/B50 | 92.0 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 86.0 °C |
| RTI Imp | UL 746 | 85.0 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 9.2E-5 cm/cm/°C |
| RTI | UL 746 | 90.0 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 75.0 °C |
| RTI Elec | UL 746 | 90.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/FR15U-NA1000 |
|---|---|---|---|
| screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.10 % | ||
| Processing (melt) temperature | 205 to 230 °C | ||
| drying temperature | 80 to 90 °C | ||
| Suggested injection volume | 50 to 70 % | ||
| drying time | 2.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 200 to 210 °C | ||
| Temperature at the rear of the barrel | 170 to 180 °C | ||
| Exhaust hole depth | 0.038 to 0.051 mm | ||
| Temperature at the front of the material cylinder | 205 to 220 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 50 to 70 °C | ||
| Spray nozzle temperature | 205 to 230 °C |