Certificates

PBT/PET EMC-130C TOYOBO JAPAN
VYLOPET®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | TOYOBO JAPAN/EMC-130C |
---|---|---|---|
Rockwell hardness | ASTM D785 | 90 M(Scale) |
Mechanical properties | Test Condition | Test Method | TOYOBO JAPAN/EMC-130C |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 63.0 J/m |
bending strength | 23°C | ASTM D790 | 150 Mpa |
Impact strength of cantilever beam gap | 泰伯磨耗试验 | ASTM D1044 | 38 mg/1000cycles |
elongation at break | 23°C | ASTM D638 | 1.5 % |
Flexural modulus | 23°C | ASTM D790 | 13000 Mpa |
tensile strength | 23°C | ASTM D638 | 110 Mpa |
Electrical performance | Test Condition | Test Method | TOYOBO JAPAN/EMC-130C |
---|---|---|---|
dielectric strength | 2.00mm | ASTM D149 | 36 KV/mm |
Dissipation Factor | 耐电弧性 | ASTM D495 | 181 S |
Volume resistivity | ASTM D257 | 1E+14 Ω.cm |
Flame retardant performance | Test Condition | Test Method | TOYOBO JAPAN/EMC-130C |
---|---|---|---|
UL flame retardant rating | UL -94 | 5VA 1.70mm | |
UL -94 | V-0 1.50mm | ||
UL -94 | V-0 3.00mm | ||
UL -94 | V-0 0.75mm |
physical property | Test Condition | Test Method | TOYOBO JAPAN/EMC-130C |
---|---|---|---|
Shrinkage rate | MD | ASTM D995 | 0.20 % |
Water absorption rate | ASTM D570 | 0.050 % | |
Shrinkage rate | TD | ASTM D995 | 0.80 % |
Thermal performance | Test Condition | Test Method | TOYOBO JAPAN/EMC-130C |
---|---|---|---|
Linear coefficient of thermal expansion | 熔点 | 255 °C | |
Heat distortion temperature | 1.80MPa未退火,HDT | ASTM D648 | 225 °C |
Linear coefficient of thermal expansion | 最大使用温度 | ASTMUL746B | 130 °C |
MD | ASTM D696 | 2.5E-05 cm/cm/°C | |
Heat distortion temperature | 0.45MPa未退火,HDT | ASTM D648 | 240 °C |