PP CL 50 E Carmel Olefins Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Carmel Olefins Ltd./ CL 50 E |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 15 kJ/m² |
| -20°C | ISO 180 | 6.0 kJ/m² |
| hardness | Test Condition | Test Method | Carmel Olefins Ltd./ CL 50 E |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 58 |
| film | Test Condition | Test Method | Carmel Olefins Ltd./ CL 50 E |
|---|---|---|---|
| tensile strength | MD:断裂,50µm,铸造薄膜 | ISO 527-3 | 39.0 MPa |
| elongation | MD:断裂,50µm,铸造薄膜 | ISO 527-3 | 470 % |
| tensile strength | MD:屈服,50µm,铸造薄膜 | ISO 527-3 | 15.0 MPa |
| elongation | MD:屈服,50µm,铸造薄膜 | ISO 527-3 | 13 % |
| tensile strength | TD:断裂,50µm,铸造薄膜 | ISO 527-3 | 41.0 MPa |
| elongation | TD:断裂,50µm,铸造薄膜 | ISO 527-3 | 1200 % |
| tensile strength | TD:屈服,50µm,铸造薄膜 | ISO 527-3 | 15.0 MPa |
| elongation | TD:屈服,50µm,铸造薄膜 | ISO 527-3 | 15 % |
| Mechanical properties | Test Condition | Test Method | Carmel Olefins Ltd./ CL 50 E |
|---|---|---|---|
| Flexural modulus | ISO 178 | 450 MPa |
| physical property | Test Condition | Test Method | Carmel Olefins Ltd./ CL 50 E |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 6.0 g/10min |