POM F20-73R1 MITSUBISHI ENGINEERING JAPAN
Iupital™ 
Electronic and Electrical Applications,Automotive sector
Weather resistance,Medium viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

machinabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F20-73R1
Mold temperature60-80 °C
Processing temperature180-210 °C
Screw speed80-120 rpm
thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F20-73R1
Combustibility (rate)UL 94HB
Linear coefficient of thermal expansionASTM D696/ISO 113591.1E-04 mm/mm.℃
mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F20-73R1
Bending modulusASTM D790/ISO 1782610 kg/cm²(MPa)[Lb/in²]
bending strengthASTM D790/ISO 17891 kg/cm²(MPa)[Lb/in²]
Elongation at BreakASTM D638/ISO 52730 %
Tensile modulusASTM D638/ISO 5272900 kg/cm²(MPa)[Lb/in²]
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F20-73R1
Arc resistanceASTM D495/IEC 60112600
Dielectric constantASTM D150/IEC 602503.9
Surface resistivityASTM D257/IEC 600931.E+16 Ω
Volume resistivityASTM D257/IEC 600931.E+12 Ω.cm
otherTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F20-73R1
characteristic中粘度 低甲醛排放
Physical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/F20-73R1
densityASTM D792/ISO 11831.41
Shrinkage rateASTM D9552.0 %
Water absorption rateASTM D570/ISO 620.22 %