PPO(PPE) Iupiace® AP6GM2 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® AP6GM2 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 7.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® AP6GM2 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Volume resistivity | IEC 60093 | 5E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® AP6GM2 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 3800 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.9 % |
| Tensile modulus | 23°C | ISO 527-2 | 4000 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 65.0 MPa |
| bending strength | 23°C | ISO 178 | 116 MPa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® AP6GM2 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® AP6GM2 |
|---|---|---|---|
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 28.0 cm³/10min |
| Shrinkage rate | TD:3.20mm | 0.30to0.50 % | |
| MD:3.20mm | 0.30to0.50 % | ||
| Water absorption rate | 饱和,23°C | ISO 62 | 0.060 % |
| density | ISO 1183 | 1.16 g/cm³ |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® AP6GM2 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 5.8E-05 cm/cm/°C |