PC+Polyester LNP™ STAT-LOY™ 63000CTC compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC/LNP™ STAT-LOY™ 63000CTC compound
Impact strength of cantilever beam gap23°CASTM D256580 J/m
Charpy Notched Impact Strength23°CISO 179/2C69 kJ/m²
Mechanical propertiesTest ConditionTest MethodSABIC/LNP™ STAT-LOY™ 63000CTC compound
elongation断裂4内部方法200 %
tensile strength 屈服3ASTM D63835.0 MPa
屈服ISO 527-2/534.0 MPa
Flexural modulus--6ISO 1781150 MPa
Tensile modulus--ISO 527-2/11190 MPa
elongation断裂ISO 527-2/5140 %
bending strength断裂,50.0mm跨距ASTM D79052.0 MPa
Flexural modulus50.0mm跨距5ASTM D7901170 MPa
Tensile modulus--2ASTM D6381170 MPa
Electrical performanceTest ConditionTest MethodSABIC/LNP™ STAT-LOY™ 63000CTC compound
Volume resistivityASTM D2578.0E+9到3.0E+11 ohms·cm
Surface ResistivityASTM D2579.0E+9到4.0E+11 ohms
StaticDecayFTMS101B2.0 sec
optical performance Test ConditionTest MethodSABIC/LNP™ STAT-LOY™ 63000CTC compound
Haze ratio2540µmASTM D100325 %
transmissivity2540µmASTM D100377.0 %
physical property Test ConditionTest MethodSABIC/LNP™ STAT-LOY™ 63000CTC compound
Shrinkage rateMD内部方法0.60 %
Water absorption rate平衡,23°C,50%RHISO 620.70 %
Shrinkage rateTD内部方法0.60 %
densityASTM D7921.16 g/cm³
Thermal performanceTest ConditionTest MethodSABIC/LNP™ STAT-LOY™ 63000CTC compound
Heat distortion temperature1.8MPa,未退火,6.40mm，HDTASTM D64875.0 °C
Linear coefficient of thermal expansionTD:23到60°CISO 11359-21.4E-04 cm/cm/°C
MD:23到60°CISO 11359-21.2E-04 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,6.40mm，HDTASTM D64884.0 °C