PA66 A4 1 natural (3716) AKRO-PLASTIC GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ A4 1 natural (3716) |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 3.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GmbH/ A4 1 natural (3716) |
|---|---|---|---|
| Flexural modulus | ISO 178 | 3000 MPa | |
| Fracture bending strain | ISO 178 | 7.0 % | |
| Tensile strain | 断裂 | ISO 527-2/50 | >30 % |
| Tensile modulus | ISO 527-2/1 | 3000 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.5 % |
| tensile strength | 屈服 | ISO 527-2/50 | 90.0 MPa |
| bending strength | ISO 178 | 125 MPa |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GmbH/ A4 1 natural (3716) |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GmbH/ A4 1 natural (3716) |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.14 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 1.8 % |
| MD | ISO 294-4 | 1.5 % | |
| Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 20.0 cm³/10min |
| Water absorption rate | 70°C | ISO 1110 | 2.4to2.8 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ A4 1 natural (3716) |
|---|---|---|---|
| melting temperature | DIN EN11357-1 | 260 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 72.0 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 52.0 °C |