Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 6370-BK1G425L SABIC INNOVATIVE US
LNP™ COLORCOMP™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/6370-BK1G425L |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 1.1E-04 cm/cm/°C |
| RTIElec | UL746 | 140 °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 2.7E-05 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 2.7E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 163 °C |
| RTIStr | UL746 | 140 °C | |
| Vicat Softening Temperature | -- | ISO306/B120 | 150 °C |
| ASTMD152512 | 153 °C | ||
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 204 °C |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 149 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 155 °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 148 °C |
| Linear thermal expansion coefficient | MD：60to138°C | ASTME831 | 2E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C | |
| Evolution Calendar intelligent importer | UL746 | 130 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/6370-BK1G425L |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 109 |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/6370-BK1G425L |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 5380 Mpa |
| Tensile Strain | 断裂 | ISO527-2/5 | 110 % |
| Tensile Modulus | ISO527-2/1 | 8500 Mpa | |
| Tensile Strain | Break | ASTMD638 | 4.0 % |
| Tensile Strength | 屈服 | ASTMD638 | 97.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 3.00 Mpa |
| Flexural Modulus | ISO178 | 7750 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 150 Mpa |
| Tensile Strain | Yield | ASTMD638 | 3.0 % |
| Flexural Strength | Break,50.0mmSpan | ASTMD790 | 138 Mpa |
| ISO178 | 154 Mpa | ||
| Tensile Modulus | ASTMD638 | 9750 Mpa | |
| Tensile Strength | Break | ASTMD638 | 91.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/5 | 3.0 % |
| Tensile Stress | 屈服 | ISO527-2/5 | 105 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/6370-BK1G425L |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| 24hr | ASTMD570 | 0.090 % | |
| Modeling Shrinkage | MD：--3 | 内部方法 | 0.40to0.50 % |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 12.0 cm3/10min |
| Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 24 g/10min |
| Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 19.0 cm3/10min |
| Specific Volume | ASTMD792 | 0.700 cm³/g | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.50 % |
| Modeling Shrinkage | TD：--2 | 内部方法 | 0.40to0.70 % |
| MD：--2 | 内部方法 | 0.30to0.40 % | |
| TD：--3 | 内部方法 | 0.70to0.90 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/6370-BK1G425L |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 6.0 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 17.0 J |
| 23°C | ISO179/1eA | 9.0 kJ/m² | |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 5.00 J |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 10 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/6370-BK1G425L |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/6370-BK1G425L |
|---|---|---|---|
| High Amp Arc Ignition | HAI | UL746 | PLC 3 |
| Volume Resistivity | ASTMD257 | 4.8E+15 ohms·cm | |
| Dielectric Constant | 100Hz | ASTMD150 | 4.00 |
| Dissipation Factor? | 1MHz | ASTMD150 | 0.020 |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 1 |
| Dissipation Factor? | 100Hz | ASTMD150 | 3E-03 |
| Dielectric Strength | 1.60mm,在油中 | ASTMD149 | 27 KV/mm |
| Dielectric Constant | 1MHz | ASTMD150 | 4.00 |
| Arc Resistance | ASTMD495 | PLC 5 | |
| Hot-wire Ignition | HWI | UL746 | PLC 1 |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 20 KV/mm |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |