Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP B130 CELANESE USA
VECTRA®
Automotive Applications、Home appliance components
High rigidity、Flame retardant、enhance、Glass fiber reinforced、Low contractility、Filler/Reinforcement Glas、Packing weight of 305、Low shrinkage rate、Good stiffness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | CELANESE USA/B130 |
|---|---|---|---|
| Limiting Oxygen Index (LOI) | ISO 4589-1-2 | 50 % |
| Basic performance | Test Condition | Test Method | CELANESE USA/B130 |
|---|---|---|---|
| density | ISO 1183 | 1600 kg/m |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/B130 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23℃ | ISO 180/1U | 15.0 KJ/m |
| Tensile creep modulus | 1hr | ISO 899-1 | 16000 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 14.0 KJ/m |
| Flexural modulus | 23℃ | ISO 178 | 20000 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 12.0 KJ/m |
| Tensile creep modulus | 1000hr | ISO 899-1 | 14100 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 18.0 KJ/m |
| Breaking stress | ISO 527-1 | 205 Mpa | |
| Tensile modulus | ISO 527-1 | 22000 Mpa | |
| Rockwell hardness | ISO 2039-2 | 100 M Scale | |
| fracture strain | ISO 527-1 | 1.0 % | |
| bending strength | 23℃ | ISO 178 | 300 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/B130 |
|---|---|---|---|
| relative permittivity | 1000Hz | IEC 60250 | 3.50 |
| dielectric strength | IEC 60243-1 | 38 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 4.00 |
| Volume resistivity | IEC 60093 | 1E+13 ohm.m | |
| Dielectric loss | 100Hz | IEC 60250 | 0.0100 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dielectric loss | 1000Hz | IEC 60250 | 0.0080 |
| physical property | Test Condition | Test Method | CELANESE USA/B130 |
|---|---|---|---|
| Shrinkage rate | parallel | ISO 2577 | 0.20 % |
| normal | ISO 2577 | 0.0 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/B130 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-1 | 250 °C |
| Linear coefficient of thermal expansion | normal | ISO 11359-1 | 0.000013 cm/cm℃ |
| parallel | ISO 11359-1 | 3E-06 cm/cm℃ | |
| combustibility | UL 94 | V-0 | |
| Heat distortion temperature | 1.80MPa，HDT | ISO 75-1 | 235 °C |
| vicat | 50℃/h 50N | ISO 306 | 169 °C |