Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS Nilac MT Soredi S.p.a.
--
Application in the automotive field
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Soredi S.p.a./Nilac MT |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 75 R |
| Mechanical properties | Test Condition | Test Method | Soredi S.p.a./Nilac MT |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 45.0 MPa |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 400 J/m |
| tensile strength | 23°C | ASTM D638 | 30.0 MPa |
| Impact strength of cantilever beam gap | 加德纳冲击 | ASTM D3029 | 40.0 J |
| Flexural modulus | 23°C | ASTM D790 | 1500 MPa |
| elongation at break | 23°C | ASTM D638 | 100 % |
| Flame retardant performance | Test Condition | Test Method | Soredi S.p.a./Nilac MT |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.60mm | |
| GWIT | 1.60mm | IEC 60695-2-12 | 550 °C |
| physical property | Test Condition | Test Method | Soredi S.p.a./Nilac MT |
|---|---|---|---|
| Shrinkage rate | MD3.0mm | ASTM D995 | 0.60 % |
| melt mass-flow rate | 220℃/10Kg | ASTM D1238 | 6.0 g/10min |
| Water absorption rate | (23°C,24hr) | ASTM D570 | 0.25 % |
| density | ASTM D792 | 1.04 g/cm³ |
| Thermal performance | Test Condition | Test Method | Soredi S.p.a./Nilac MT |
|---|---|---|---|
| vicat | ASTM1525 | 98.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 9E-05 cm/cm／°C |
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | 70.0 °C |