TPE DUPONT USA 4069

Extrusion grade

US$ 7,620 / MT

FOB Guangzhou port, China

flammability	Test Condition	Test Method	DUPONT USA/4069
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	20 %
UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
UL flame retardant rating		1.5mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	<100 mm/min
UL flame retardant rating	3.0mm	UL 94	HB
FMVSS flammability		FMVSS302	B
Physical properties	Test Condition	Test Method	DUPONT USA/4069
Water absorption rate	23°C,24hr	ISO 62	0.70 %
density		ISO 1183	1.11 g/cm³
Shrinkage rate	MD	ISO 294-4	0.80 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.70 %
Shrinkage rate	TD	ISO 294-4	0.80 %
MediumDensity			1.10 g/cm³
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.30 %
melt mass-flow rate	220°C/2.16kg	ISO 1133	8.5 g/10min
Melt Volume Flow Rate (MVR)	220°C/2.16kg	ISO 1133	8.80 cm3/10min
mechanical properties	Test Condition	Test Method	DUPONT USA/4069
Tensile strain	Break	ISO 527-2	>300 %
Tensile modulus		ISO 527-2	45.0 Mpa
tensile strength	50%Strain	ISO 527-2	6.70 Mpa
Nominal tensile fracture strain		ISO 527-2	800 %
Bending modulus		ISO 178	45.0 Mpa
tensile strength	10%Strain	ISO 527-2	3.20 Mpa
tensile strength		Break	ISO 527-2	29.0 Mpa
Electrical performance	Test Condition	Test Method	DUPONT USA/4069
Dissipation factor	100Hz	IEC 60250	0.013
Volume resistivity		IEC 60093	4E+12 ohms·cm
Dissipation factor	1MHz	IEC 60250	0.020
Relative permittivity	100Hz	IEC 60250	4.80
Surface resistivity		IEC 60093	3E+14 ohms
Relative permittivity	1MHz	IEC 60250	4.70
Dielectric strength		IEC 60243-1	18 KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 0
elastomer	Test Condition	Test Method	DUPONT USA/4069
tear strength	Flow	ISO 34-1	100 kN/m
tear strength		横向Flow	ISO 34-1	100 kN/m
Supplementary Information	Test Condition	Test Method	DUPONT USA/4069
Odor		VDA270	4.00
EmissionofOrganicCompounds		VDA277	10.0 µgC/g
impact performance	Test Condition	Test Method	DUPONT USA/4069
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	-40°C	ISO 179/1eA	NoBreak
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 180/1A	NoBreak
Impact strength of cantilever beam gap		-40°C	ISO 180/1A	NoBreak
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	23°C	ISO 179/1eA	NoBreak
film	Test Condition	Test Method	DUPONT USA/4069
Water vapor permeability	23°C,85%RH,25μm	DIS15106-1/-2	900 g/m²/24hr
thermal performance	Test Condition	Test Method	DUPONT USA/4069
Linear coefficient of thermal expansion	TD：--	ISO 11359-2	2E-04 cm/cm/°C
Linear coefficient of thermal expansion		TD：-40to23°C	ISO 11359-2	2.8E-04 cm/cm/°C
Melting temperature		ISO 11357-3	193 °C
Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	2.8E-04 cm/cm/°C
Brittle temperature		ISO 974	-96.0 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	2.2E-04 cm/cm/°C
Glass transition temperature		ISO 11357-2	-50.0 °C
hardness	Test Condition	Test Method	DUPONT USA/4069
Shore hardness	ShoreD,15Sec	ISO 868	33
Shore hardness		ShoreD	ISO 868	37