Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML6411-76701 SABIC INNOVATIVE US
LEXAN™
Electrical appliances、Architectural Application、Plastic bag、Lighting applications
Easy to form、Short molding cycle、Low temperature and high
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML6411-76701 |
|---|---|---|---|
| RTI | UL 746 | 100 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 119 °C |
| 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 128 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 8 | ISO 75-2/Ae | 115 °C | |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 5.9E-5 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO 306/B120 | 135 °C |
| RTI Elec | UL 746 | 100 °C | |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 7.7E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 8 | ISO 75-2/Be | 125 °C |
| Vicat Softening Temperature | -- | ASTM D15259, ISO 306/B509 | 134 °C |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI Imp | UL 746 | 100 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 114 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/ML6411-76701 |
|---|---|---|---|
| Suggested Max Moisture | 0.020 % | ||
| Middle Temperature | 250 到 290 °C | ||
| Processing (Melt) Temp | 270 到 300 °C | ||
| Drying Time | 2.0 到 4.0 hr | ||
| Rear Temperature | 230 到 260 °C | ||
| Nozzle Temperature | 250 到 290 °C | ||
| Drying Temperature | 90 到 100 °C | ||
| Front Temperature | 260 到 300 °C | ||
| Hopper Temperature | 60 到 80 °C | ||
| Mold Temperature | 60 到 90 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/ML6411-76701 |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/2.16 kg | ASTM D1238 | 7.0 g/10 min |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.10 % |
| Melt Volume flow Rate | 260°C/5.0 kg | ISO 1133 | 18.0 cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.30 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML6411-76701 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO 527-2/50 | 58.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 2350 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 100 % |
| Tensile Strength | 屈服 3 | ASTM D638 | 62.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 5.0 % |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2600 Mpa |
| Tensile Modulus | -- 2 | ASTM D638 | 2500 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/50 | 62.0 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 95.0 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 5.0 % |
| Flexural Stress | -- 5, 6 | ISO 178 | 90.0 Mpa |
| Flexural Modulus | -- 5 | ISO 178 | 2350 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 100 % |
| Tensile Strength | 断裂 3 | ASTM D638 | 54.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML6411-76701 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 72.0 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/ML6411-76701 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA |
| 3.0 mm, Testing by SABIC | UL 94 | 5VA | |
| Glow Wire Ignition Temperature | 2.0 mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 2.0 mm | UL 94 | 5VB |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 3.0 mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML6411-76701 |
|---|---|---|---|
| Hot-wire Ignition | UL 746 | PLC 3 | |
| Dielectric Strength | 3.20 mm, in Oil | ASTM D149 | 27 KV/mm |
| Comparative Tracking Index | UL 746 | PLC 2 | |
| High Amp Arc Ignition | UL 746 | PLC 1 | |
| Volume Resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC 60112 | 250 V |