Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS LG9000 SABIC INNOVATIVE US
CYCOLAC™
Automotive sector
UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 320 J/m |
| 23°C | ASTM D256 | 530 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 40.7 J |
| -30°C,TotalEnergy | ASTM D3763 | 33.9 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 75 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 84.8 Mpa |
| tensile strength | 屈服 | ASTM D638 | 54.5 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2310 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| gloss | 60°,无织构 | ASTM D523 | 30 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.10 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 17 g/10min |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.40 % |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50-0.70 % |
| density | ASTM D792 | 1.13 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 110 °C |
| Linear coefficient of thermal expansion | TD：-20to150°C | ASTME831 | 7.2E-05 cm/cm/°C |
| vicat | ASTM D15254 | 129 °C | |
| thermal conductivity | ASTMC177 | 0.20 W/m/K | |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 124 °C |
| RTI Imp | UL 746 | 60.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 129 °C |
| RTI Str | UL 746 | 60.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 107 °C |
| RTI Elec | UL 746 | 60.0 °C |