PC/ABS C3650-111 SABIC INNOVATIVE NANSHA
CYCOLOY™
Shell、Electronic and electrical
High mobility、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C3650-111 |
|---|---|---|---|
| Thermal Conductivity | ISO8302 | 0.20 W/m/K | |
| RTIElec | UL746 | 60.0 °C | |
| RTIStr | 60.0 °C | ||
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 88.9 °C |
| Vicat Softening Temperature | -- | ISO306/B120 | 110 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| MD：23到60°C | ISO11359-2 | 8E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 91.0 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 108 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 100 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| TD：23to60°C | ISO11359-2 | 8E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 102 °C |
| Evolution Calendar intelligent importer | UL746 | 60.0 °C | |
| Vicat Softening Temperature | ASTMD152510 | 110 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C3650-111 |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 113 Mpa |
| Rockwell Hardness | R级 | ISO2039-2 | 124 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C3650-111 |
|---|---|---|---|
| Moisture Absorption | 饱和,23°C | ASTMD570 | 0.60 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.60 % |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 8.00 cm3/10min |
| Melt Mass-Flow Rate | ASTMD1238 | 8.5 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C3650-111 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2690 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 55.0 Mpa |
| Tensile Elongation | ASTMD638 | 35 % | |
| Tensile Strain | ISO527-2/5 | 55 % | |
| ISO527-2/50 | >50 % | ||
| Tensile Modulus | ISO527-2/1 | 2600 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 64.8 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 50.0 Mpa |
| Flexural Modulus | ISO178 | 2700 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 101 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 4.9 % |
| Tensile Stress | ISO527-2/50 | 65.0 Mpa | |
| Tensile Strain | 4.5 % | ||
| Flexural Strength | ISO178 | 100 Mpa | |
| Tensile Modulus | ASTMD638 | 2860 Mpa | |
| Tensile Strength | 断裂 | 51.0 Mpa | |
| Tensile Strain | 屈服 | ISO527-2/5 | 3.0 % |
| Tensile Stress | 55.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C3650-111 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 13 kJ/m² |
| Charpy Notched Impact Strength | ISO179/1eA | 13 kJ/m² | |
| Notched Izod Impact Strength | 0°C | ISO180/1A | 15 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 65.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 48 kJ/m² |
| Notched Izod Impact Strength | ISO180/1A | 45 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C3650-111 |
|---|---|---|---|
| Oxygen Index | ISO4589-2 | 37 % | |
| Flame Rating | 1.5mm | UL94 | V-0 |
| 2.5mm | 5VB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C3650-111 |
|---|---|---|---|
| Dielectric Strength | 1.60mm,在油中 | IEC60243-1 | 25 KV/mm |
| Dissipation Factor? | 50Hz | ASTMD150 | 6E-03 |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor? | 60Hz | ASTMD150 | 6E-03 |
| Comparative Tracking Index | IEC60112 | 600 V | |
| Dissipation Factor? | 60Hz | IEC60250 | 4E-03 |
| 50Hz | 4E-03 | ||
| 1MHz | 6E-03 | ||
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| 0.800mm,在油中 | 35 KV/mm | ||
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 60Hz | IEC60250 | 2.80 |
| 1MHz | 2.70 | ||
| 50Hz | 2.80 |