PC EXL1330 WH SABIC INNOVATIVE US
LEXAN™ 
sporting goods、Aerospace Applications、Electrical appliances、Plastic bag
Middle flow、Ductility at low temperat、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 WH
RTIUL 746120 °C
Deflection Temperature Under Load?1.8 MPa, 未退火, 6.40 mmASTM D648124 °C
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10ISO 75-2/Ae125 °C
Linear thermal expansion coefficient横向 : -40 到 40°CASTM E8316.7E-5 cm/cm/°C
Vicat Softening Temperature--ISO 306/B120145 °C
RTI ElecUL 746125 °C
Linear thermal expansion coefficient流动 : -40 到 40°CASTM E8316.7E-5 cm/cm/°C
Vicat Softening Temperature--ASTM D152511, ISO 306/B5011143 °C
Linear thermal expansion coefficient横向 : 23 到 80°CISO 11359-27.2E-5 cm/cm/°C
Deflection Temperature Under Load?0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10ISO 75-2/Be136 °C
Ball PressureTest123 到 127°CIEC 60695-10-2通过
Linear thermal expansion coefficient流动 : 23 到 80°CISO 11359-27.2E-5 cm/cm/°C
RTI ImpUL 746115 °C
Deflection Temperature Under Load?1.8 MPa, 未退火, 3.20 mmASTM D648120 °C
0.45 MPa, 未退火, 3.20 mmASTM D648134 °C
HardnessTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 WH
Ball Indentation HardnessH 358/30ISO 2039-190.0 Mpa
InjectionTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 WH
Middle Temperature280 到 305 °C
Drying Time3.0 到 4.0 hr
Suggested Shot Size40 到 60 %
Drying Temperature120 °C
Mold Temperature70 到 95 °C
Vent Depth0.025 到 0.076 mm
Suggested Max Moisture0.020 %
Processing (Melt) Temp295 到 315 °C
Rear Temperature215 到 295 °C
Nozzle Temperature290 到 310 °C
Front Temperature295 到 315 °C
Back Pressure0.300 到 0.700 Mpa
Screw Speed40 到 70 rpm
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 WH
Moisture Absorption平衡, 23°C, 50% RHISO 620.15 %
Melt Mass-Flow Rate300°C/1.2 kgASTM D123810 g/10 min
Modeling Shrinkage横向流动 : 3.20 mm内部方法0.40 到 0.80 %
流动 : 3.20 mm内部方法0.40 到 0.80 %
Moisture Absorption饱和, 23°CISO 620.35 %
Melt Volume flow Rate300°C/1.2 kgISO 11339.00 cm3/10min
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 WH
Tensile Strength断裂ISO 527-2/5056.0 Mpa
Tensile Modulus--ISO 527-2/12100 Mpa
Tensile Elongation断裂 3ASTM D638130 %
Tensile Strength屈服 3ASTM D63858.0 Mpa
Tensile Elongation屈服ISO 527-2/505.0 %
Flexural Modulus50.0 mm 跨距 4ASTM D7902060 Mpa
Tensile Modulus-- 2ASTM D6382100 Mpa
Tensile Strength屈服ISO 527-2/5055.0 Mpa
Flexural Stress屈服, 50.0 mm 跨距 4ASTM D79088.0 Mpa
Tensile Elongation屈服 3ASTM D6386.0 %
Flexural Stress-- 5, 6ISO 17885.0 Mpa
Flexural Modulus-- 5ISO 1782100 Mpa
Tensile Elongation断裂ISO 527-2/50> 100 %
Tensile Strength断裂 3ASTM D63861.0 Mpa
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 WH
Unnotched Izod Impact Strength23°CISO 180/1U无断裂
Instrumented Dart Impact23°C, Total EnergyASTM D376352.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA60 kJ/m²
23°CISO 179/1eA75 kJ/m²
Charpy Unnotched Impact Strength23°CISO 179/1eU无断裂
Unnotched Izod Impact Strength-30°CISO 180/1U无断裂
Charpy Unnotched Impact Strength-30°CISO 179/1eU无断裂
FlammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 WH
Glow Wire Ignition Temperature1.0 mmIEC 60695-2-13875 °C
Glow Wire Flammability Index0.8 mmIEC 60695-2-12850 °C
Oxygen IndexISO 4589-235 %
Glow Wire Flammability Index1.0 mmIEC 60695-2-12960 °C
UL flame retardant rating0.8 mmUL 94HB
Glow Wire Ignition Temperature3.0 mmIEC 60695-2-13875 °C