Certificates
PA46 TW200F6 DSM HOLAND
Stanyl®
Electronic and electrical、Casters
Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DSM HOLAND/TW200F6 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 290 °C |
| RTI Elec | 0.9 mm | UL 746 | 140 °C |
| Melting Temperature | ISO 11357-3 | 295 °C | |
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 290 °C |
| Linear thermal expansion coefficient | 流动 | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 6.0E-5 cm/cm/°C | |
| IEC 60216 | 177 °C |
| Physical | Test Condition | Test Method | DSM HOLAND/TW200F6 |
|---|---|---|---|
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 2.6 % |
| Density | ISO 1183 | 1.41 g/cm³ | |
| Modeling Shrinkage | 横向流量 | ISO 294-4 | 1.3 % |
| 流量 | ISO 294-4 | 0.50 % |
| Mechanical Properties | Test Condition | Test Method | DSM HOLAND/TW200F6 |
|---|---|---|---|
| Tensile Stress | 断裂, 160°C | ISO 527-2 | 100 Mpa |
| 断裂, 180°C | ISO 527-2 | 95.0 Mpa | |
| Tensile Modulus | -- | ISO 527-2 | 10000 Mpa |
| 120°C | ISO 527-2 | 5500 Mpa | |
| Flexural Modulus | -- | ISO 178 | 9000 Mpa |
| Tensile Strain | 断裂, 200°C | ISO 527-2 | 7.5 % |
| Tensile Stress | 断裂, 200°C | ISO 527-2 | 90.0 Mpa |
| Tensile Strain | 断裂 | ISO 527-2 | 4.0 % |
| Tensile Modulus | 180°C | ISO 527-2 | 4400 Mpa |
| 160°C | ISO 527-2 | 5000 Mpa | |
| Flexural Modulus | 120°C | ISO 178 | 4700 Mpa |
| Tensile Modulus | 200°C | ISO 527-2 | 4000 Mpa |
| Flexural Modulus | 160°C | ISO 178 | 3900 Mpa |
| Tensile Stress | 断裂, 120°C | ISO 527-2 | 110 Mpa |
| 断裂 | ISO 527-2 | 210 Mpa | |
| Tensile Strain | 断裂, 120°C | ISO 527-2 | 7.5 % |
| 断裂, 160°C | ISO 527-2 | 7.5 % | |
| 断裂, 180°C | ISO 527-2 | 7.5 % |
| Impact Properties | Test Condition | Test Method | DSM HOLAND/TW200F6 |
|---|---|---|---|
| Notched Izod Impact Strength | -40°C | ISO 180/1A | 11 kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 65 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| 23°C | ISO 179/1eA | 12 kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO 180/1A | 12 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 80 kJ/m² |
| Flammability | Test Condition | Test Method | DSM HOLAND/TW200F6 |
|---|---|---|---|
| Flammability level | 0.75 mm | IEC 60695-11-10, -20 | HB |
| 1.5 mm | IEC 60695-11-10, -20 | HB |
| Electrical Properties | Test Condition | Test Method | DSM HOLAND/TW200F6 |
|---|---|---|---|
| Relative Permittivity | 100 Hz | IEC 60250 | 4.30 |
| Dielectric Strength | IEC 60243-1 | 30 KV/mm | |
| Relative Permittivity | 1 MHz | IEC 60250 | 4.00 |
| Volume Resistivity | IEC 60093 | 1.0E+14 ohms·cm | |
| Comparative Tracking Index | IEC 60112 | 300 V |