PPS A604 BK TORAY SHENZHEN

Torelina®

sporting goods,Automotive sector,Electronic field,Electrical field

High temperature resistan,Glass fiber reinforced,Flame retardant,Filler: Glass fiber reinf,40% filler by weight

Plastic Datasheets

hardness	Test Condition	Test Method	TORAY SHENZHEN/A604 BK
Rockwell hardness	R-Scale	ISO 2039-2	122

Supplementary Information	Test Condition	Test Method	TORAY SHENZHEN/A604 BK
BarFlowLength	320°C,1.00mm	Internal Method	165 mm

thermal performance	Test Condition	Test Method	TORAY SHENZHEN/A604 BK
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	3.5E-05 cm/cm/°C
Linear coefficient of thermal expansion		MD	ISO 11359-2	2.3E-05 cm/cm/°C
Melting temperature		ISO 11357-3	278 °C

mechanical properties	Test Condition	Test Method	TORAY SHENZHEN/A604 BK
Bending modulus	23°C	ISO 178	15000 Mpa
bending strength	23°C	ISO 178	290 Mpa
Friction coefficient			0.25
shear strength	23°C	JISK7214	75.0 Mpa
Taber abraser	1000Cycles	ISO 9352	50.0 mg
Tensile strain	Break,23°C	ISO 527-2	1.7 %
tensile strength	Yield,23°C	ISO 527-2	190 Mpa

Electrical performance	Test Condition	Test Method	TORAY SHENZHEN/A604 BK
Dielectric constant	23°C,1MHz	IEC 60250	3.60
Dielectric strength		IEC 60243-1	25 KV/mm
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
Volume resistivity		IEC 60093	1E+16 ohms·cm

Physical properties	Test Condition	Test Method	TORAY SHENZHEN/A604 BK
Shrinkage rate	TD:3.00mm2	Internal Method	0.80 %
Shrinkage rate		MD:3.00mm4	Internal Method	0.20 %
Water absorption rate	23°C,24hr	ISO 62	0.020 %

impact performance	Test Condition	Test Method	TORAY SHENZHEN/A604 BK
Impact strength of simply supported beam without notch	23°C	ISO 179	45 kJ/m²

flammability	Test Condition	Test Method	TORAY SHENZHEN/A604 BK
UL flame retardant rating	0.200mm	UL 94	V-0