HDPE CA6132 Cabot Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Cabot Corporation/ CA6132 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 65 kJ/m² |
| hardness | Test Condition | Test Method | Cabot Corporation/ CA6132 |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | ASTM D2240 | 64 |
| Electrical performance | Test Condition | Test Method | Cabot Corporation/ CA6132 |
|---|---|---|---|
| Surface Resistivity | 内部方法 | 2.1E+02 ohms | |
| Volume resistivity | 内部方法 | 63 ohms·cm |
| Mechanical properties | Test Condition | Test Method | Cabot Corporation/ CA6132 |
|---|---|---|---|
| tensile strength | 屈服,模压成型 | ISO 527-2 | 20.6 MPa |
| 断裂,模压成型 | ISO 527-2 | 27.4 MPa | |
| Tensile strain | 断裂,模压成型 | ISO 527-2 | 920 % |
| Flexural modulus | ISO 178 | 838 MPa |
| physical property | Test Condition | Test Method | Cabot Corporation/ CA6132 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 2.5to3.5 % |
| melt mass-flow rate | 190°C/10.0kg | ISO 1133 | 0.60 g/10min |
| density | 23°C | 内部方法 | 1.05 g/cm³ |
| melt mass-flow rate | 190°C/21.6kg | ISO 1133 | 3.6 g/10min |
| Thermal performance | Test Condition | Test Method | Cabot Corporation/ CA6132 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 41.0 °C |
| vicat | ISO 306/A | 126 °C |