density

ISO1183

g/cm³

1

Melt Volume-Flow Rate (MVR)

250°C/2.16kg

ISO1133

cm3/10min

1

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

Viscosity value

降低的粘度

ISO1628

ml/g

1

Charpy Notched Impact Strength

23°C

ISO179

kJ/m²

6

Charpy Notched Impact Strength

-30°C

ISO179

kJ/m²

6

Impact strength of simply supported beam without notch

23°C

ISO179

kJ/m²

3

Tensile modulus

23°C

ISO527-2

Mpa

6

tensile strength

断裂,23°C

ISO527-2

Mpa

1

elongation

断裂,23°C

ISO527-2

%

2

Bending modulus

23°C

ISO178

Mpa

6

Impact strength of cantilever beam gap

-30°C

ISO180

kJ/m²

6

Impact strength of cantilever beam gap

23°C

ISO180

kJ/m²

6

RTI Imp

0.40mm

UL746

°C

7

RTI Imp

0.75mm

UL746

°C

1

RTI Imp

1.5mm

UL746

°C

1

RTI Imp

3.0mm

UL746

°C

1

RTIElec

3.0mm

UL746

°C

1

RTIElec

0.40mm

UL746

°C

7

RTIElec

0.75mm

UL746

°C

1

RTIElec

1.5mm

UL746

°C

1

RTIStr

0.40mm

UL746

°C

7

RTIStr

0.75mm

UL746

°C

1

RTIStr

1.5mm

UL746

°C

1

RTIStr

3.0mm

UL746

°C

1

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

2

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

1

Melting temperature

ISO3146

°C

2

Volume resistivity

IEC60093

ohms·cm

>