Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM F25-63 KEP KOREA
KEPITAL®
--
Good liquidity、copolymer、wear resistant、Low friction coefficient、Medium to low viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | KEP KOREA/F25-63 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179 | 6.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | KEP KOREA/F25-63 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 32 % | |
| Tensile stress | ISO527-2/50 | 63.0 Mpa | |
| Flexural modulus | 23°C | ISO178 | 2500 Mpa |
| Bending stress | 23°C | ISO178 | 85.0 Mpa |
| Electrical performance | Test Condition | Test Method | KEP KOREA/F25-63 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+16 ohms | |
| Volume resistivity | IEC60093 | 1E+16 ohms·cm | |
| dielectric strength | IEC60243-1 | 19 KV/mm |
| physical property | Test Condition | Test Method | KEP KOREA/F25-63 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.20 % |
| melt mass-flow rate | 190°C/2.16kg | ISO1133 | 15 g/10min |
| Shrinkage rate | MD1：3.00mm | 内部方法 | 2.0 % |
| density | ISO1183 | 1.41 g/cm³ |
| Thermal performance | Test Condition | Test Method | KEP KOREA/F25-63 |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/A | 100 °C | |
| melting temperature | ISO11357-3 | 165 °C |