ABS AG10NP FCFC TAIWAN
TAIRILAC®
Household appliances、Helmet、Electronic field、Electrical field、Extruded molded products、Helmet、Tubular products.
High rigidity、Cold resistance、heat-resisting、Toughening、 Used for extrusion moldi、Ultra high impact resista、High rigidity
UL
MSDS
Processing
TDS
UL
RoHS
SVHC
PSC
CSA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | FCFC TAIWAN/AG10NP |
|---|---|---|---|
| melt mass-flow rate | 220℃×10kgf(98N) | ASTM D-1238(ISO 1133) | 6.5 g/10min |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AG10NP |
|---|---|---|---|
| Flexural modulus | 23℃ | ASTM D-790(ISO 178) | 25000(2450) kg/cm2(MPa) |
| bending strength | 23℃ | ASTM D-790(ISO 178) | 740(73) kg/cm2(MPa) |
| tensile strength | 23℃ | ASTM D-638(ISO 527) | 490(48) kg/cm2(MPa) |
| Impact strength of cantilever beam gap | 23℃1/4"厚 | ASTM D-256(ISO R180) | 46(451) kg.cm/cm(J/m) |
| Rockwell hardness | 23℃ | ASTM D-785(ISO 2039/2) | R-102 |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AG10NP |
|---|---|---|---|
| density | 23℃/23℃ | ASTM D-792(ISO 1183) | 1.04 |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AG10NP |
|---|---|---|---|
| Hot deformation temperature (HDT) | Annealed(8℃×8hr)，HDT | ASTM D-648(ISO 75/A) | 104 °C |
| vicat | 1Kg load | ASTM D-1525(ISO 306) | 107 °C |
| Hot deformation temperature (HDT) | Unanneaied 18.6kg/cm²(1/2"厚），HDT | ASTM D-648(ISO 75/A) | 92 °C |