Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PS SUPREME HIPS SH400M Supreme Petrochem Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Supreme Petrochem Ltd./SUPREME HIPS SH400M |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm,注塑 | ASTM D256 | 85 J/m |
| Mechanical properties | Test Condition | Test Method | Supreme Petrochem Ltd./SUPREME HIPS SH400M |
|---|---|---|---|
| Flexural modulus | 23°C,3.20mm,注塑 | ASTM D790 | 2000 MPa |
| tensile strength | 23°C,3.20mm,注塑 | ASTM D638 | 29.0 MPa |
| bending strength | 23°C,3.20mm,注塑 | ASTM D790 | 45.0 MPa |
| elongation | 断裂,23°C,3.20mm,注塑 | ASTM D638 | 20 % |
| optical performance | Test Condition | Test Method | Supreme Petrochem Ltd./SUPREME HIPS SH400M |
|---|---|---|---|
| gloss | 60°,3200µm,注塑 | ASTM D523 | 92 |
| flammability | Test Condition | Test Method | Supreme Petrochem Ltd./SUPREME HIPS SH400M |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Supreme Petrochem Ltd./SUPREME HIPS SH400M |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 4.0 g/10min |
| density | ASTM D792 | 1.03 g/cm³ |
| Thermal performance | Test Condition | Test Method | Supreme Petrochem Ltd./SUPREME HIPS SH400M |
|---|---|---|---|
| vicat | ASTM D15254 | 99.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,注塑，HDT | ASTM D648 | 79.0 °C |