PBT B4040G6 HRBK BASF GERMANY
Ultradur®
Automotive External Parts,Shell,printed circuit board,Application in the automotive field,Industrial components
Filler: Glass fiber reinf,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B4040G6 HRBK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 48 kJ/m² |
| -30°C | ISO 179/1eU | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B4040G6 HRBK |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.1 % |
| tensile strength | 断裂 | ISO 527-2 | 140 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B4040G6 HRBK |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 4.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 1.6E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.80 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.017 |
| flammability | Test Condition | Test Method | BASF GERMANY/B4040G6 HRBK |
|---|---|---|---|
| Flammability level | 1.6mm | IEC 60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/B4040G6 HRBK |
|---|---|---|---|
| Apparent density | 0.70to0.80 g/cm³ | ||
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 33.0 cm3/10min |
| Shrinkage rate | free,longitudinal | 0.14 % | |
| TD | ISO 294-4 | 1.0 % | |
| MD | ISO 294-4 | 0.31 % | |
| viscosity number | ISO 307 | 85.0 cm³/g | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Shrinkage rate | free,transverse | 0.88 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B4040G6 HRBK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 223 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 2.5E-5到3.5E-5 cm/cm/°C |
| maximum service temperature | 短周期操作 | 210 °C |