Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM M90CF2001 CELANESE NANJING
Celcon®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE NANJING/M90CF2001 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.0 kJ/m² |
| -30°C | ISO 179/1eA | 6.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 190 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.7 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 180 kJ/m² |
| Electrical performance | Test Condition | Test Method | CELANESE NANJING/M90CF2001 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| IEC 60093 | 8E+14 ohms·cm | ||
| Surface Resistivity | IEC 60093 | 3E+16 ohms |
| Mechanical properties | Test Condition | Test Method | CELANESE NANJING/M90CF2001 |
|---|---|---|---|
| tensile strength | Yield,71°C | ASTM D638 | 34.5 Mpa |
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 10 % |
| tensile strength | 屈服,-40°C | ASTM D638 | 94.5 Mpa |
| Tensile creep modulus | 1hr | ISO 899-1 | 2450 Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 2760 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1350 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2550 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 60.7 Mpa |
| 屈服 | ISO 527-2/1A/50 | 65.0 Mpa |
| physical property | Test Condition | Test Method | CELANESE NANJING/M90CF2001 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
| DensityMelt | 内部方法 | 1.200 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.75 % | |
| density | ISO 1183 | 1.41 g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | 2.2 % |
| TD | ISO 294-4 | 1.9 % | |
| SpecificHeatCapacity of Melt | 内部方法 | 2210 J/kg/°C | |
| Shrinkage rate | MD | ISO 294-4 | 2.0 % |
| ThermalConductivityofMelt | 内部方法 | 0.16 W/m/K | |
| density | ASTM D792 | 1.41 g/cm³ | |
| Shrinkage rate | TD | ASTM D955 | 1.8 % |
| melt mass-flow rate | ASTM D1238 | 9.0 g/10min |
| Thermal performance | Test Condition | Test Method | CELANESE NANJING/M90CF2001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| melting temperature | ISO 11357-3 | 165 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 158 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 101 °C | |
| melting temperature | ASTM D3418 | 165 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| Effective thermal diffusivity coefficient | 内部方法 | 0.0485 cSt | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.2E-04 cm/cm/°C |