PA/ABS A2508 DAICEL JAPAN
NOVALLOY-A
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | DAICEL JAPAN/A2508 |
|---|---|---|---|
| Rockwell hardness | 23℃ | 116to118 |
| thermal performance | Test Condition | Test Method | DAICEL JAPAN/A2508 |
|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火 | °C | 106to202 |
| Vicat softening temperature | °C | 107to181 |
| mechanical properties | Test Condition | Test Method | DAICEL JAPAN/A2508 |
|---|---|---|---|
| elongation | 断裂,23℃ | % | 3.8to4.0 |
| Fracture, 23 ℃ | 51.03to124.14 MPa | ||
| Tensile modulus | 23℃ | 2503.45to5400.0 MPa | |
| Yield, 23 ℃ | 43.03to56.41 MPa |
| Physical properties | Test Condition | Test Method | DAICEL JAPAN/A2508 |
|---|---|---|---|
| Flow: 23 ℃ | 流动,23℃ | mm/mm | 76.2E-3-127.0E-3 |
| Water absorption rate | 23℃,24hr | % | 0.70 |
| impact performance | Test Condition | Test Method | DAICEL JAPAN/A2508 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 6.500to11.143 |